Ultraform® S 2320 003 UNC Q600 聚甲醛（POM）共聚物 BASF Corporation Web |
| 产品说明 | |
Ultraform S 2320 003 UNC Q600 is an easy flowing and rapidly freezing injection molding POM grade. Contains a mold release agent. | |
| 总体 | |
材料状态 |
|
资料 1 | Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
UL 黄卡 2 | |
搜索 UL 黄卡 | BASF CorporationUltraform® |
供货地区 |
|
添加剂 |
|
性能特点 |
|
用途 |
|
机构评级 | EC 1907/2006 (REACH)FDA 21 CFR 177.2470 |
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
多点数据 | Isochronous Stress vs. Strain (ISO 11403-1)Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Specific Heat vs. Temperature (ISO 11403-2)Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | |||
-- | 1.40 | g/cm3 | ASTM D792 |
-- | 1400 | kg/m3 | ISO 1183 3 |
熔体体积流动速率 (190°C/2.16 kg) | 11.0 | cm3/10min | ISO 1133 3 |
收缩率 | |||
流动: 3.18 mm | 2.0 | % | ASTM D955 |
横向流量 | 2.1 | % | ISO 294-4 |
流量 | 2.1 | % | ISO 294-4 |
吸水率 | |||
饱和 | 0.80 | % | ASTM D570, ISO 62 3 |
平衡, 50% RH | 0.20 | % | ASTM D570 |
平衡 | 0.20 | % | ISO 62 3 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 2700 | MPa | ISO 527-2 3 |
抗张强度 | |||
屈服, 23°C | 65.0 | MPa | ASTM D638 |
屈服, -40°C | 93.0 | MPa | ISO 527-2 |
屈服, 80°C | 33.0 | MPa | ISO 527-2 |
屈服 | 65.0 | MPa | ISO 527-2 3 |
伸长率 | |||
屈服, 23°C | 9.0 | % | ASTM D638 |
屈服 | 9.0 | % | ISO 527-2 3 |
断裂伸长率 | 28 | % | ISO 527-2 3 |
拉伸蠕变模量 | ISO 899-1 3 | ||
1 hr | 1900 | MPa | |
1000 hr | 1300 | MPa | |
弯曲模量 (23°C) | 2620 | MPa | ASTM D790 |